204-1(A)substitute type antirust oil

  

Name:204-1-substitute Type Antirust Oil

Product Component
This product is produced by taking the refined mineral oil as the base oil and compounding many kinds of antirust additives such as the sulfonated lanoline calcium soap. Does not contain heavy metals, belongs to environmental protection type antirust oil.

Product Characteristic
1. Strong antirust property, good anti- salt mist performance, thin, transparent and artistic oil film, 2 years steel antirust time, the copper's antirust time may for a year (in the room and packed).
2. Do not need to heat up the oil, can directly use the cold coating method in order to improve environment and reduce the labor intensity.
3. Has good replacement ability to the hand sweat

Use:
This product is suitable for the bearing, the measuring instrument, the automobile fitting, the fastener's processing and the steel products's oil seal antirust, also may use for the metallurgical industry steel products' oil seal antirust and the antirust between tools.
Directions For Use:
This product has wet mould and baked mould kinds, the baked mould is oily paste form, must add two time of 120# benzin or kerosene to dilute before use. The wet mould has diluted already, can use directly, it is produced by taking the refined low viscosity machinery oil as the base oil and then specially processed into the end product; it does not volatilize and is noninflammable; before coat the oil or soak , the components or the steel products which need the antirust must carry on the clean and dehydrated processing.
Quality Standard: SY1576-80
Quality Index:

Item

Index

Test Method

Oil base stability

qualified

test by eyes

Moisture( % )≤

trace

GB260

Salt spray test:(day) 35 ± 1 °C 0 grade

sheet steel ≥

10

SH/T0081

copper sheet ≥

7

Heat and moisture test:(day) 49 ± 1 °C 0 grade

sheet steel ≥

30

GB/T2361

cast iron sheet ≥

10

copper sheet ≥

7

lamination Test(day) 49 ± 1 °C 0 grade

sheet steel ≥

7

SY1576

cast iron sheet ≥

5

copper sheet ≥

7

Corrosion test( 7 days)

sheet steel( 0 grade)

qualified

SY2752

copper sheet ( 1 grade)

sweat substitution property:( 1 day)

sheet steel

qualified

SY2754

Packing and Storage
Wet Mould: 170kg iron drum;baked mould:15kg tinplate quadrate bottle. Please store in room under the temperature of 0-40°C;avoid blending with water and other rabbish.